ESAB offers a complete line of welding and cutting products and solutions. Explore our equipment offering with ease based on product line and industry.
ESAB is a world leader in welding and cutting equipment and consumables. Explore our complete line of welding & cutting products for virtually every application.
ESAB University Courses are incremental, structured learning modules designed to help you take your skills to the next level. New courses are being added regularly, so please check back often. Click the link to see current courses offered.
Articles cover industry topics more in-depth and are created in partnership with ESAB engineers and master welders. Click the links to see the latest.
Tips from ESAB Experts to help take your welding, cutting and fabrication skills to the next level.
ESAB Courses are structured learning designed to help welders achieve certain learning milestones and explore topics more in-depth. Check back often for updated resources.
ESAB University videos are curated with tips and best practices from top fabricators around the world. Learn new techniques or improve your current skills with ESAB University videos.
Enhance your knowledge of welding, cutting, and fabrication with free and accessible webinars on a variety of topics, including welding best practices, tips for using ESAB products, new product launches, and more, presented by trusted ESAB experts.
ESAB is a world leader in welding and cutting equipment and consumables. We offer a complete line of fabrication solutions for virtually every application.
ESAB Newsroom - Stay up to date with the latest news from ESAB. View press releases, product announcements, corporate news, and more here.
ESAB EHS (Environment, Health & Safety) initiatives are monitored with the highest degree of importance and commitment to safety is ingrained in our culture.
The history of ESAB is the History of Welding. Go here to view an interactive look at ESAB's history in shaping the future of innovation in welding, cutting, and fabrication.
View available job openings and more on the ESAB Careers page.
ESAB is recognised for its adherence to the best industry practices and commitment to its employees and customers. Explore our list of prestigious awards that we have been honoured with!
Purchasing from an ESAB Authorised Distributor guarantees you first-class customer service and support for all ESAB products.
ESAB offers a wealth of product support resources, including a range of technical and service publications, from Safety Data Sheets and downloadable product manuals to product certifications.
Visit ESAB's global manual search engine to access the items below and more.
Global User Manuals
Instruction Manuals
Spare Parts List
Product Storage Instructions
View Main Contact Page
View ESAB Location Information
+91 44 4228 1100
No playlist found! Your playlist can be created here.
Filler Metals
Most welders experience difficulty welding dissimilar metals. An example of it is weld fusion on ferritic-to-carbon-steel joints - the welds do not seem to be fusing with the carbon steel. This problem is not uncommon when welding stainless steel (SS) to carbon steel. In many cases, it can be resolved simply by removing any mill scale or surface impurities from the base materials. Keep in mind that the surface of stainless steel has a tough oxide layer that makes it passive to environmental attack. This oxide can sometimes cause welding difficulties.
In the present article, we will focus on the potential problems welding dissimilar metals such as ferritic to carbon steel. We will also discuss welding dissimilar metals using 309 stainless steel.
Let us consider a case where the welder is experiencing issues welding ferritic stainless steel and other grades of stainless steel (SS) with carbon steel.
The welding team commonly builds and welds carbon steel parts with a standard ER 70S-6 wire using a 98 percent argon/2 percent carbon dioxide shielding gas. Recently they have begun manufacturing parts that combine carbon steel, ferritic stainless steel, and other grades of stainless steel (SS) using a 309LSi grade of wire with GMAW (Gas Metal Arc Welding). The welders are struggling with weld fusion on the ferritic-to-carbon-steel joints - the welds do not seem to be fusing with the carbon steel. The welding team is looking for suggestions on it.
In most cases when welding dissimilar metals or, more specifically, carbon to SS, we recommend you use a 309 filler metal because of its higher ferrite content. This higher ferrite content can minimize weld dilution and prevent weld cracking. The 309LSi grade of wire has a low carbon content and a higher silicon content, hence the "LSi" in the designator. The lower carbon content is ideal for applications that have a risk of intergranular corrosion cracking. The higher silicon content serves as a deoxidizer and helps remove weld impurities and increase weld puddle fluidity.
When welding carbon steel to SS, be some weld dilution from the sides of the joint will occur. The small amount of base material dilution in the weld metal will provide a better match to each of those respective base materials. You should not have difficulties welding on the ferritic side of the joint as stainless-to-stainless welding should fuse relatively well. If there are problems, check to ensure the welding machine is set up correctly with good work lead connections.
The 309LSi weld issues on the carbon steel may be the result of contamination. Try cleaning the steel with an approved cleaner to remove any grease, oil, or paint. Grinding the mill scale ½ inch back from the weld joint may also help.
Last, the 98 percent argon/2 percent CO2 may not be aggressive enough to allow for proper weld bead wetting on the carbon steel side of the joint. You want to keep the CO2 low to minimize carbon pickup in the weld joint and prevent the welds from oxidizing too much. However, since there is already cross-contamination from welding on the carbon steel, using a higher-CO2 mix, such as 90/10 or even 85/1, may provide the necessary oxidizing action to allow the weld to tie in properly.