ESAB offers a complete line of welding and cutting products and solutions. Explore our equipment offering with ease based on product line and industry.
ESAB is a world leader in welding and cutting equipment and consumables. Explore our complete line of welding & cutting products for virtually every application.
ESAB University Courses are incremental, structured learning modules designed to help you take your skills to the next level. New courses are being added regularly, so please check back often. Click the link to see current courses offered.
Articles cover industry topics more in-depth and are created in partnership with ESAB engineers and master welders. Click the links to see the latest.
Tips from ESAB Experts to help take your welding, cutting and fabrication skills to the next level.
ESAB Courses are structured learning designed to help welders achieve certain learning milestones and explore topics more in-depth. Check back often for updated resources.
ESAB University videos are curated with tips and best practices from top fabricators around the world. Learn new techniques or improve your current skills with ESAB University videos.
Enhance your knowledge of welding, cutting, and fabrication with free and accessible webinars on a variety of topics, including welding best practices, tips for using ESAB products, new product launches, and more, presented by trusted ESAB experts.
ESAB is a world leader in welding and cutting equipment and consumables. We offer a complete line of fabrication solutions for virtually every application.
ESAB Newsroom - Stay up to date with the latest news from ESAB. View press releases, product announcements, corporate news, and more here.
ESAB EHS (Environment, Health & Safety) initiatives are monitored with the highest degree of importance and commitment to safety is ingrained in our culture.
The history of ESAB is the History of Welding. Go here to view an interactive look at ESAB's history in shaping the future of innovation in welding, cutting, and fabrication.
View available job openings and more on the ESAB Careers page.
ESAB is recognised for its adherence to the best industry practices and commitment to its employees and customers. Explore our list of prestigious awards that we have been honoured with!
Purchasing from an ESAB Authorised Distributor guarantees you first-class customer service and support for all ESAB products.
ESAB offers a wealth of product support resources, including a range of technical and service publications, from Safety Data Sheets and downloadable product manuals to product certifications.
Visit ESAB's global manual search engine to access the items below and more.
Global User Manuals
Instruction Manuals
Spare Parts List
Product Storage Instructions
View Main Contact Page
View ESAB Location Information
+91 44 4228 1100
No playlist found! Your playlist can be created here.
Filler Metals
One of the key factors in welding is selecting the suitable filler alloy based on the requirement. Let us consider a case where the welder needs to select the most suitable filler alloy for a particular GMAW (Gas Metal Arc Welding) welded aluminum structure.
The welder is looking for some assistance with the selection of the most suitable filler alloy for a particular GMAW welded aluminum structure. The component is used for material handling manufactured from 6061-T6 in material thicknesses of 1/8 to 1/2 inch. The joint design is fillet weld.
Special Operating Considerations: The selected welding filler alloy should be suitable for sustained high-temperature application (250°F), provide good structural integrity, and suitable feedability characteristics. This component is to be used in the as-welded condition and will not undergo any post weld heat treatment.
The sustained high-temperature application (above 150°F) requirement for this component is probably the main consideration and will most definitely influence the filler alloy selection. Also, as this component is intended to be used for handling material and the welds being used are fillet welds, you need to certainly consider the shear strength characteristics of the filler alloy.
The high service temperature requirement eliminates the use of any filler alloy with more than 3% Mg such as the frequently used 5356 and the higher strength filler alloys 5183 and 5556. This provides you with 4643, 4043, 4047, and 5554 as possible filler alloys for your application.
To find out the most appropriate filler alloy let us evaluate each of these four filler alloys based on their features and characteristics.
Considerations relating to four filler alloys that may be used for this application: 4643, 4043, 4047, and 5554.
This filler alloy was developed for welding 6xxx series base alloys and developing high mechanical properties in the post-weld heat-treated condition. This alloy was produced by taking the well-known alloy 4043, reducing the silicon, and adding 0.10 to 0.30 percent magnesium, thus ensuring its ability to respond to post-weld heat treatment. This is a premium filler alloy that is priced for its specialized characteristics and would not normally be used unless post weld heat treating was being performed. As post weld heat treatment is not to be used, there is no reason to use this alloy.
While the 4043 filler alloy, a 5% Silicon alloy, is often used to weld 6061 base materials, it is not commonly used when the shear strength of the component is a predominant consideration. The 4043 filler alloy is a silicon-based filler alloy that is often used to take advantage of the element’s capability of promoting fluidity in aluminum. While groove welds can be made using this filler alloy that can characteristically pass minimum transverse tensile test requirements, this filler alloy has considerably lower shear strength when compared to the 5xxx series filler alloys.
Like the 4043 filler alloy, 4047 is a silicon-based alloy but has a much higher level of silicon, approximately 12%. The extra silicon within the alloy provides exceptional fluidity. This alloy, which is also registered as a brazing alloy, is most often used for leak-tight joints in thin-wall applications. The 4047 filler alloy has a very narrow freezing range and consequently is very resistant to solidification cracking. The 4043 and 4047 filler alloys have remarkably similar mechanical characteristics - 4047 having slightly higher tensile strength. Both 4043 and 4047 have lower ductility and lower shear strength properties than the 5xxx series filler alloys. They also possess lower column strength when compared to the 5xxx series filler alloys, and consequently, require extra care during feeding to minimize feedability problems.
The 5554 filler alloy was designed to provide the improved strength and ductility characteristics of a magnesium-based filler alloy that was also suitable for elevated temperature applications. It contains 2.4% to 3.0% magnesium thereby providing an alloy that is not susceptible to stress corrosion cracking but has improved shear strength and improved ductility when compared to the 4xxx series filler alloys. The typical transverse shear strength of 4043 and 4047 is 15.0 ksi and the typical transverse shear strength of 5554 is 23 ksi, an increase of 65% (see Fig 1).
In addition to the improved mechanical properties of 5554 on the completed weld, we see an increase in the column strength of the wire. This characteristic can distinctly improve the wire feedability. The 5554 filler alloy will typically produce a weld that is not as cosmetically appealing as the 4xxx series filler alloys and has a slightly greater potential for producing “smut” (a black deposit of metal oxides that is not harmful to the weld).
Typical Shear Strength of fillet welds.
Filler alloy 4643 was designed for its post weld heat treatment capabilities and is therefore not particularly suited for your application.
Filler alloys 4043 and 4047 have considerably lower shear strength values when compared to 5554.
Filler alloys 4043 and 4047 wire have considerably lower tensile (column) strength and require more care when feeding when compared to 5554.
Filler alloy 4047 may provide some advantages over 4043: enhanced fluidity, the possibility of faster welding speeds, and lower heat input. This filler alloy may be a consideration for thinner components and produces excellent leak-tight joints.
Filler alloy 5554 will typically provide welds of higher strength but with lower cosmetic appeal when compared to the 4xxx series filler alloys.