ESAB offers a complete line of welding and cutting products and solutions. Explore our equipment offering with ease based on product line and industry.
ESAB is a world leader in welding and cutting equipment and consumables. Explore our complete line of welding & cutting products for virtually every application.
ESAB University Courses are incremental, structured learning modules designed to help you take your skills to the next level. New courses are being added regularly, so please check back often. Click the link to see current courses offered.
Articles cover industry topics more in-depth and are created in partnership with ESAB engineers and master welders. Click the links to see the latest.
Tips from ESAB Experts to help take your welding, cutting and fabrication skills to the next level.
ESAB Courses are structured learning designed to help welders achieve certain learning milestones and explore topics more in-depth. Check back often for updated resources.
ESAB University videos are curated with tips and best practices from top fabricators around the world. Learn new techniques or improve your current skills with ESAB University videos.
Enhance your knowledge of welding, cutting, and fabrication with free and accessible webinars on a variety of topics, including welding best practices, tips for using ESAB products, new product launches, and more, presented by trusted ESAB experts.
ESAB is a world leader in welding and cutting equipment and consumables. We offer a complete line of fabrication solutions for virtually every application.
ESAB Newsroom - Stay up to date with the latest news from ESAB. View press releases, product announcements, corporate news, and more here.
ESAB EHS (Environment, Health & Safety) initiatives are monitored with the highest degree of importance and commitment to safety is ingrained in our culture.
The history of ESAB is the History of Welding. Go here to view an interactive look at ESAB's history in shaping the future of innovation in welding, cutting, and fabrication.
View available job openings and more on the ESAB Careers page.
ESAB is recognised for its adherence to the best industry practices and commitment to its employees and customers. Explore our list of prestigious awards that we have been honoured with!
Purchasing from an ESAB Authorised Distributor guarantees you first-class customer service and support for all ESAB products.
ESAB offers a wealth of product support resources, including a range of technical and service publications, from Safety Data Sheets and downloadable product manuals to product certifications.
Visit ESAB's global manual search engine to access the items below and more.
Global User Manuals
Instruction Manuals
Spare Parts List
Product Storage Instructions
View Main Contact Page
View ESAB Location Information
+91 44 4228 1100
No playlist found! Your playlist can be created here.
Filler Metals
You can weld aluminum to most metals easily through adhesive bonding or mechanical fastening. However, to weld aluminum to steel, special techniques are required.
Directly arc welding metals such as steel, copper, magnesium, or titanium to aluminum produces very brittle intermetallic compounds. To avoid this, you must isolate the other metal from the molten aluminum during the process.
There are three common techniques that can be used to successfully weld aluminum to steel.
Creating bimetallic transition inserts is a popular method used when welding aluminum to steel. This method is often used for producing welded connections of excellent quality within structural applications.
The bimetallic transition inserts are sections of material comprising of one-part aluminum with equal part steel or stainless steel. The inserts are already bonded to the aluminum. Various methods are used to bond these dissimilar materials and form the bimetallic transition. These methods include rolling, explosion welding, friction welding, flash welding (or hot pressure welding), and arc welding.
Arc welding the steel and aluminum bimetallic transition inserts is done through normal methods of GMAW or GTAW. One side of the insert is welded steel to steel. The other is welded aluminum to aluminum.
Performing an aluminum-to-aluminum weld first helps prevent the inserts from overheating. This also provides a larger heat sink when the steel-to-steel weld is performed.
The bimetallic transition insert method is commonly used to:
Another method many use to successfully weld aluminum to steel is dip coating. This is also commonly referred to as hot-dip aluminizing. In this method, the steel is coated with aluminum prior to welding the steel and aluminum together.
Once coated, the steel member can be arc welded to the aluminum member. Care should be taken to prevent the arc from impinging on the steel. A specific technique must be used during welding to direct the arc onto the aluminum member. The technique also allows the molten aluminum from the weld pool to flow into the aluminum-coated steel.
Another coating method for welding aluminum to steel is brazing. It involves coating the steel surface with silver solder. The pieces are then welded together using aluminum filler alloy.
Please note that neither of these coating-type joint methods (dip coating, brazing) are typically depended on for full mechanical strength. They are usually used for sealing purposes only.
If you want to learn more about welding aluminum to steel, or if you have a question that was not answered here, please feel free to contact us.